Alternative to Hot dip Galvanizing for Household Gas Tanks
November 27, 2017
Q. Hi folk.
Company Managing Director - New Zealand
We are making household gas tanks which were to be hot dip galvanized, but China is no longer permitting galvanizing activities (pollution issue).
Our factory wants to supply the goods coated as follows as an alternative.
"First layer >40 micron thick zinc rich primer containing over 90% zinc. Second layer resin top coat >40 microns. Total surface coating >80 micron".
How far short of galvanizing is would this surface be?
What better/new alternatives could we use to best replace hot dip galvanizing?
This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site
Disclaimer: It's not possible to diagnose a amadeya42 problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.
If you need a product/service, please check these Directories:
JobshopsCapital Equip. & Install'nChemicals & Consumables
Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices
©1995-2018 amadeya42.com, Inc., Pine Beach, NJ - -