Silver Flashing vs Tin Plating of Switchgear Bus Bar

A discussion started in 2004 but continuing through 2018


Q. I am the Quality Assurance Manager for a manufacturing company in Southeast Texas. We manufacture switchgear and various other products for marine and industrial use. Our switchgear ranges from 600VAC to 15KVAC, and from 0 to 6000 Amps. At one time we primarily used tin plated copper bus bars; however, with industry changes we have since moved to silver flashed copper bus bars.

Recently we shipped some switchgear from the US to Singapore, and when the customer uncrated the switchgear, s/he found silver flashed copper bus that appears to have begun oxidizing/corroding. We are unsure of the cause at this time; however, we have shipped many products overseas with no reported incidents.

silver plated copper bus bars

My question(s) are as follows:

1. Is silver flashing better/worse than tin plating? Why?
2. Which one, if either begins to tarnish/oxidize sooner, given the same weather conditions?
3. What is the recommended thickness of both?

I would like the answers to get a better understanding as to why copper bars are plated/flashed, is silver better than tin, why is that, the similarities/differences, and to prevent this situation from repeating.

Steve W [last name deleted for privacy by Editor]
swithgear - Beaumont, Texas


A. Dear Mr. Steve,

The coating of Silver in this case appears to have been too thin, I presume its Copper that we are seeing below the busbar. Whatever the Silver thickness, you must use an anti-tarnish over Silver. The minimum should be 3 to 6 microns.

The prediction about Silver vs. tin corrosion resistance is like this: You can probably afford to put on 10 microns of tin for every micron of Silver at the same cost. 10 microns of Tin will outdo 1 micron of Silver hands down. Fixed Busbars like yours are traditionally only Tin plated + anti tarnished; only moving parts that are likely to arc are generally silver plated.

Khozem Vahaanwala
Khozem Vahaanwala
Saify Ind supporting advertiser
Bangalore, Karnataka, India

saify logo


Q. It appears we are going to move back to using tin plated copper bus bars for our switchgear. The next question is what is the "standard" or recommended plating/flashing thickness of tin? What is it for silver?

Steve W [returning]
swithgear - Beaumont, Texas, United States


A. I have plated busbars to a spec of 5 - 12 microns of Tin. You have to determine your plating thickness requirement based upon "Fitness of use" for your current / corrosion requirements. I do not believe that anyone else's spec may work for you!

Khozem Vahaanwala Khozem Vahaanwala
Saify Ind
Bangalore, Karnataka, India


Q. We are also tin plating switchgear busbars. We use an 8 micron finish of acid tin, we also send parts to hot climates with no reports of corrosion. One problem we do have is a milky finish on our busbars. analysis shows no faults with the solution. I cannot understand why we get this "milky" result so often, the busbars are typically up to 1800 mm long and 200 mm wide copper busbars, any help would be appreciated

Shaun Moore
- Kent, UK


A. Have you ensured that your Tin plating bath was always under 27 °C? You may have lost some of your stannous.

Khozem Vahaanwala Khozem Vahaanwala
Saify Ind
Bangalore, Karnataka, India

(2007) -- this entry appended to this thread by editor in lieu of spawning a duplicative thread

Q. Please let me know what shall be the thickness of tin coating used in copper bus?

Sujoy Roy
Electrical Engineer - Philadelphia, Pennsylvania, USA

February 17, 2008 -- this entry appended to this thread by editor in lieu of spawning a duplicative thread

Q. We are manufacturing switchgear in Saudi Arabia. Could you please advise us about the minimum thicknesss of the silver and tin plating of the busbar as per the international standard?

Engr. Hussam Al-Sakka
production mgr., switchgear - Dammam, Saudi Arabia

Ed. note: Sujoy, Hussam. We appended your questions to a thread where they are already answered. Get back to us if you have additional questions.

October 11, 2010

Q. Which is the best, silver or tin plated?

Jim Raub
Switchgear engineer - crosby, Texas USA

December 28, 2012

A. Hi Jim. Please see Khozema Vahanwala's first response -- I found it very informative.


Ted Mooney, amadeya42.com Teds signature
Ted Mooney, P.E.
Pine Beach, New Jersey

April 11, 2013

A. I'm not in the plating business, but rather in the electrical design and installation side of the industry.
What I have noticed is that in a high H2S (Hydrogen sulfide) environment copper and silver have a high oxidation rate in a short period of time.

I have had generators fail because the silver solder holding the winding retaining bars oxidized completely away allowing the windings to flex under load and short.

This was a gas plant with 200,000 PPM H2S in the inlet stream.

Tin is not affected.

Just sharing.

Tony Romero
- Katy, Texas USA

December 28, 2012

Q. Dear receiver

We are switch board assembling company and we have a difficulty with bus bar corrosion and discoloration.
We have no idea about the necessary chemicals to avoid above.
With regard to tin plating on bus bars, I want to know the chemical to be applied or any other method to use to do this.

electromech engineering - Maharagama, Sri Lanka

A. Hi. The chemical to be applied is tin electroplating solution, but it's not a chemical that is wiped on or brushed on like a paint; rather, it's a manufacturing process where the bus bar is alkaline cleaned by immersion, rinsed, acid activated by immersion, rinsed, electroplated by application of DC electricity while the parts are immersed in a solution of stannous sulfate or potassium stannate (for example -- there are other choices) with proprietary addition agents, rinsed, and immersed in a bath of tarnish inhibitor.

The normal way this is done is by sending the parts to a plating jobshop. That is not to say that you absolutely can't do it in-house; but that requires a knowledge base, a significant capital investment, and probably operating and waste generation permits. Good luck.


Ted Mooney, amadeya42.com
Teds signature
Ted Mooney, P.E.
Pine Beach, New Jersey

Must Aluminum Bus Bar be Copper or Silver Plated?

November 6, 2015

Q. Hi.
I'm connecting Al 1100 bus bar to a MOD by copper/silver plated flexi-link.
The flexi-link is bolted on both ends.
The welders are saying Al cannot be bolted to flexi-link because it is copper and so the Al should be silver plated or we will have corrosion

Could you give me any direction?

Hesam Far
- Grand Rapids, Michigan, USA

November 2015

"No-Ox-Id" Compound

A. Hi Hesam. The theory they are explaining is that aluminum corrodes easily and doesn't comprise a good contact surface, so it should be copper plated and possibly silver plated before bolting. But a good answer unfortunately requires experience in the particular field you are inquiring about; for example ...

Decades ago the plating equipment supply company I was employed by made "workbars" ("flightbars") for plating & anodizing by simply bolting copper plates to extruded aluminum structural members after wire brushing and applying an anti-oxidation compound, and they functioned well enough. But that doesn't necessarily mean the method will function well enough in a different application. Good luck.


pic of Ted Mooney
Ted Mooney, P.E. RET
Pine Beach, New Jersey
Striving to live "Aloha"

February 10, 2016

Q. If the silver plated bus bar starts to Tarnish is there any chemical solution to remove the tarnish without removing the bus bar and sending for re-plating?

Ehab Radwan
switchgear - Dammam Saudi Arabia

February 2016

Twinkle Silver Polish (12 boxes)

A. Hi Ehab. Offhand, I don't see any reason to suspect that generic silver polish, used to remove tarnish from household flatware and silver would not work fine. Good luck.


pic of Ted Mooney
Ted Mooney, P.E. RET
Pine Beach, New Jersey
Striving to live "Aloha"

September 23, 2016

Q. What if the tarnish is very heavy for the silver flashed busbar? is there any chemical composition that can remove the tarnished layer?

Raveek shan
- Maharashtra, mumbai,India

October 2016

A. Hi Raveek. I have not tried it on busbar, but contact with aluminum foil in a warm or hot solution made conductive with TSP or similar chemicals is used on jewelry and silverware to cause a reduction process which converts the tarnished silver back to silver metal. Please see letter 4785 for the theory and details.

I don't see any reason this couldn't work on busbar, although the details might take a bit of effort. Maybe get an aluminum bristle scrub brush and a bucket of strong hot TSP solution and see what the scrubbing does for you? Good luck.


pic of Ted Mooney
Ted Mooney, P.E. RET
Pine Beach, New Jersey
Striving to live "Aloha"

October 6, 2016

Q. Dear Sir

I am working in EGYPT at LV SWG Manufacturer co.
We faced some cases at Busbar assembly, that breaker have contacts tin plated and the main busbar silver plated .

If there is technical problem for conductivity to connect silver with tin plate .

Appreciated your kind reply

Thanks and regards

Mohamed Abdelaziz
SWG manufacturer - Cairo, Cairo, Egypt

October 2016

A. Hi Mohamed. As someone from the electroplating field, with some plating and corrosion knowledge, I don't personally foresee a particular reason to anticipate that such a joint would be problematical. But in most specialized fields we are not limited to theoretical predictions, but we have standards and design codes that have been developed from decades of experience around the world. I don't have any experience in switchgear application, so I would certainly suggest that you investigate your company and industry standards before deciding that it is okay. This sounds like it would be a pretty common question that switchgear manufacturers have encountered hundreds of times. Good luck.


pic of Ted Mooney
Ted Mooney, P.E. RET
Pine Beach, New Jersey
Striving to live "Aloha"

Top Articles

old wood burning stoves best aluminum wheel polish conductive metal lowes tin ceiling non conductive wedding ring dog eye wash homemade best roof sealant for shingles qalo ring vs saferingz off white toilet white roof shingles mold smell in house skin rash fingers painting roof tiles cost agno3 + cu removing a bath refrigerator dent removal how to clean silver plate with baking soda 999 silver

Protecting silver plated bus bar from tarnish

January 4, 2018

Q. Hi
I am electroplating engineer in Saudi Arabia I am working in switchgear company we are facing problem in silver plated bus bar color will tarnish within the one or two weeks after production kindly advice how to protect silver tarnish

irshad alam
switchgear company - riyadh, saudi arabia

January 10, 2018

A. Irshad, what is the substrate metal (under the silver). If it is copper then tarnishing is expected. This is especially true in less than normal atmospheric conditions and higher temperatures. Please let us know the substrate or underplate.

Mark Baker
Process Engineering - Phoenix, Arizona USA

This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site


Disclaimer: It's not possible to diagnose a amadeya42 problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices

©1995-2018 amadeya42.com, Inc., Pine Beach, NJ - -