Teflon coating of stainless steel

A discussion started in 2000 & continuing through 2017


Q. I work in a watch company and we are having a problem with one of our straps. The strap is made of 316L stainless steel and is sandblasted with a special blend of coloured sand to achieve a matte and grayish finish. The sandblasted pieces were coated with a very thin layer of PU (polyurethane) coating.

The problem with this finish is scratches show up very easily, which our customers don't like. One solution from our vendor is to coating the pieces with a thicker PU coating but the straps are shinier than before. I'm not sure whether the coating really helps to reduce scratches, or the scratches are just less obvious on such finish. What are the advantages and disadvantages in such an application?

WY Wong
- Hong Kong


A. You can put a water based Teflon coating instead of a thick PU coating for your application. Water based Teflon coating is very easy to use. It produces a very thin layer of coating that has good wear resistance, non-scratchable, good chemical resistance and heat resistance.

S. Y. Yuen
- Hong Kong, China


Q. I work in a portable measuring instruments company, and we need to put PU coating on stainless steel, is there some special requirements for the part surface, and how about the process of PU coating and equipment? Thanks in advance!

Fei Peng
- Shenzhen, Guangdong, China


Q. I'd like to manufacture a product in SS306 and I want to coat it with Teflon coating.

My condition is: The SS tube with OD 4.6 mm and length 310 mm. I'd like to coat Teflon coating thickness of 20 microns on OD throughout length.

Purpose: Anti corrosion, non conductivity of heat and non conductivity of electric current.

Area of application: Pharmaceutical / Surgical.

1. Please let me know the best method of Teflon coating considering my area of application.?
2. Is there any specification for Teflon coating, surface finish, hardness, etc.? If so, what purpose it will be used?

With regards,

M. Mahendran
- Coimbatore, Tamil Nadu, INDIA


A. Coating the OD is absolutely no problem. Typical two coat Teflon coating is 35 microns +/- 10 microns. Lower thickness can be archived with good coating practices.

It will serve the purpose of anti-corrosion, heat transfer and electrical insulation (to some extent only).

However, if the application is surgical, then Dupont specifically restricts use of Teflon®. Prior clearance will be necessary from Dupont on selection of grades and the application process.

Hope this helps you.

Gurvin Singh
Coatec India
supporting advertiser
Mohali, Punjab, India
coatec india

June 18, 2008

Q. Hello,

I need to coat a SS-316 rod (currently coated with epoxy powder coating) of 60 cm length & 6 mm dia with Teflon, over the powder coating.

I need to use it for a prototype design.

It should meet the following demands
- Environment of application is oil & salt water
- Need to get electrical insulation

- Need to know how long it will last, if it is used in a water flow region?

- What should be the coating thickness to withstand such a rough condition?

Isaac Jacob
student - India

sidebar November 10, 2009

A. Try PEEK Coating instead.

William Maghen
- Bayan Lepas, Penang, Malaysia

June 27, 2010

Thanks William, but we don't know whether you are suggesting that PEEK (Polyether ether ketone) coatings would be better than Teflon for Wong's watches ... or better than PU for Fey's portable measuring instruments ... or for Mahendran's pharmaceutical/surgical application ... or better than Teflon over the epoxy on Isaac's rods :-( And in what ways would they be better? Thanks.


Ted Mooney, amadeya42.com
Teds signature
Ted Mooney, P.E.
Pine Beach, New Jersey

June 1, 2012

Q. I am interested in a thin coating of a low coefficient of friction material for stainless steel sheet metal, to prevent metal to metal contact and act as a smooth surface when components are slid against each other. Minimal load bearing on the surface.

Brian LeNlanc
- West Berlin, New Jersey

June 25, 2012

A. Depending if it has to be permanent and very long lasting or is only for occasional contact and short periods the possibilities are so vast and range from the cheapest special greases to mid-cost treatments like Teflon spray, to more expensive platings to the most expensive and exotic composites deposited by PVD, CVD, Thermospray, Plasma, etc.
G. Marrufo - Mexico

Guillermo Marrufo
Monterrey, NL, Mexico

June 30, 2012

A. Teflon adhesion to stainless steel is a problem. However, it was sorted out when Gillette introduced their Teflon coated razor blades and put down an interlayer of Pt-Cr onto their stainless steel blades. This is well patented and documented, but in essence, the process involved vacuum deposition of the Pt-Cr followed by spray coating and sinter polymerisation of PTFE. The adhesion mechanism is believed to go through a Cr-F complex structure, although I am not sure of its details.

trevor crichton
Trevor Crichton
R&D practical scientist
Chesham, Bucks, UK

January 31, 2013

Q. Can we coat Teflon coating of 70 microns on SS304 material? If so what is temperature that needs to be maintained for curing.


Thin Opaque Dip-able coating for stainless steel

March 3, 2014

Q. A handful of years ago I was shown a thin, dip-able coating applied to a stainless steel bicycle spoke which was opaque, had very good color, and was so thin that cleanly coated the fine threads of the spoke allowing the nipple to thread on without issue. Even white was very bright with no stainless showing through, on a coating that seemed to be microns thick. We chose to go another direction and I've not thought about it again until recently as I need a thin disable coating for a part with threads.

Supposedly the finish was 'sol-gel' and was being performed in Taiwan and was commonly used in manufacturing electronics, that is really all I remember about it.

Now, I've been involved in composites manufacture for a long time and am familiar with sol-gel processing for aluminum (Boegel, AC-130), but this is clearly something completely different.

Essentially, I need a very thin, dip-able cosmetic coating and can't for the life of me seem to figure out what what I'm actually looking for!

Many thanks in advance for your help

Josh Poertner
Product Engineer - Indianapolis, Indiana
br />

March 2014

A. Hi Josh. My understanding is that sol-gel coatings were most used for thin films on electronics in the beginning, but that they are now applied to glass, plastics, and metal as functional coatings. Although I have no real experience with them, it would not surprise me if you had seen TiO2 sol-gel coatings, as I'd expect them to be both white, and useful as a metal protector.

Although they are dip-able, I don't think I'd categorize them as low technology . . . by which I suggest that competitive thin coatings that are not "simple dip coatings", like electrophoretic lacquering, PVD coatings, or anodizing may sound more complex but may actually be just as "simple" and inexpensive, or more so :-)


Ted Mooney, amadeya42.com
Teds signature
Ted Mooney, P.E.
Pine Beach, New Jersey

April 28, 2015

Q. I would like to know how to give a teflon coating of 2-3 mm thickness outside a 40NB schedule 40 ss pipe, flanged at one end. Kindly advice if any enterprise is supplying the same for service as dip pipe for feeding 98% H2SO4 to treatment tank (many other chemicals are being added to tank, pH variation till 9 will occur during the process (maximum operating temperature 90 °C ).
I would have used just teflon, but there is a high speed agitator in the tank and I assume using just teflon pipe won't survive that turbulence for so long.
Thanks in advance

Arjun Vishnu
chemical industry - kerala,india
^- Sorry, this RFQ is outdated
View Current RFQs

July 23, 2015

Q. I work in a Gas control system company, and I need to put teflon coating on stainless steel 430F material, for avoiding corrosion as the part/assembly has to work on open environment and also it faces more than 250 °C temperature, hence the part gets easily corroded. and is there any alternate way to avoid corrosion please suggest if possible.
Basic need:
1)should avoid corrosion
2)coating thickness should be 5-10 micron(as part is too small)


Top Articles

how do you remove glue from plastic metal conductivity chart how to remove glue from metal surface truck wheel polisher silver nitrate compound how to clean silver coins at home how many grams in a troy ounce of gold red rings on hands why are metals good conductors of electricity fixing dents with dry ice how to clean arthur court lowes tin ceiling tiles how to clean the outside of a wood stove aluminum tank polishing how to wash out eyes boric acid solution for eyes

Teflon coatings on formed metal strips

April 27, 2016

Q. Hi All,

I want to add a teflon coating to a formed metal strip for a medical device, the strip comes in contact with the body. Can the teflon be added after^before the strip is formed? or will it crack?

Thank you in advance.

Wayne Farrar
Engineer - Manchester, UK

June 21, 2016

A. It would be best to coat this after forming masking can be used. Also you need to be more specific than Teflon this is just a trade name for a range of products but i suspect you will be wanting the P.F.A powder over a primer.

Paul Rennison
Surface technology - Leeds, Yorkshire, United kingdom

November 5, 2016

Q. I have a requirement of teflon coating (~40 microns or more) a SS304 cylinder of 11 mm outer diameter, 9 mm inner diameter, length 11 mm. Any schemes please ??

srinivasan Ranganathan
- hyderabad, india

Teflon Coating of Sintered Metal

December 19, 2017

Is PTFE coating possible in a sinter metal (mostly steel) part? I have a requirement like a housing made of SM processing needs teflon/PTFE coating.

Pramodh C Murali
- Tamilnadu, India

December 26, 2017

A. Hi,
The suggested process should not be a problem but keep in mind line-of-sight restrictions in terms of i.d. or cavity coverage, if applicable.

blake kneedler
Blake Kneedler
Feather Hollow Eng.
Stockton, California

December 29, 2017

Q. I have to do PTFE coating on a 200 dia roller; my required thickness is 8 to 10 mm. Later it has to be milled for cavities used as a rotary moulding die. Is this technically possible and which is the best method?

Ajith Parakkuth
B tech project - Chennai India

This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site


Disclaimer: It's not possible to diagnose a amadeya42 problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices

©1995-2018 amadeya42.com, Inc., Pine Beach, NJ - -